Superabsorbent polymer having improved absorption rate and absorption under pressure

ABSTRACT

A carboxylic containing superabsorbent polymer having a swell rate of at least 0.3 g./g.sec., a gel strength of about 40,000 to about 150,000 dynes/cm 2 , a centrifuge capacity at 30 minutes of about 20 to about 50 g/g, an absorption permeability under pressure at 60 minutes of at least 5 g/g at wherein the ratio of the absorption permeability under pressure at 15 minutes is at least 25% of the absorption permeability under pressure at 60 minutes is disclosed. The superabsorbent polymer is prepared from a solution of carboxylic containing monomers, a cross linking agent, and a blowing agent. The polymer is subsequently treated with a surface crosslinking agent.

This application is a division of application Ser. No. 08/405,680, filed Mar. 17, 1995, which is a continuation in part of our application Ser. No. 08/181,931 filed Jan. 18, 1994, now U.S. Pat. No. 5,399,591 which in turn is a division of Ser. No. 8/123,561, filed Sep. 17, 1993 now U.S. Pat. No. 5,314,420.

FIELD OF THE INVENTION

The present invention relates generally to superabsorbent polymers exhibiting the ability to retain high permeability to aqueous fluids under applied pressure where the permeability is not aided by gravity or by a hydrostatic head. Polymers described and claimed hereunder have a swollen gel permeability at 60 minutes of at least 5 g/g, preferably at least 15 g/g, and most preferably at least 20 g/g as measured by a test method described herein. The super absorbent materials described and claimed herein are prepared by polymerizing an acrylic acid monomer mixture in the presence of a cross linking agent and a blowing agent. The resultant materials are then surface crosslinked.

BACKGROUND OF THE INVENTION

Superabsorbent polymers are water insoluble, hydrogel-forming polymers capable of absorbing large quantities of aqueous fluids including synthetic urine, brines, and biological fluids such as urine, sweat, and blood, while retaining the absorbed fluids under pressure. Hydrogel-forming super-absorbent polymers are useful as absorbents for water and aqueous body fluids when the polymers are incorporated in absorbent articles, such as disposable diapers, adult incontinence pads, sanitary napkins, and bandages. Many of the existing superabsorbents are formed from unsaturated carboxylic acid monomers including acrylic acid, methacrylic acid, alkylacrylates, and acrylamides which are rendered water insoluble by crosslinking.

The degree of crosslinking affects the absorbent capacity and gel strength of a superabsorbent. Absorbency is a measure of the mount of fluid which a given mount of superabsorbent polymer will absorb. Gel strength indicates the tendency of the hydrogel once formed to deform under an applied stress. Polymers exhibiting inadequate gel strength will form a hydrogel which deforms and fills the void space in an absorbent article, inhibiting absorbent capacity and fluid distribution throughout the article. Polymers having low absorbent capacity are incapable of absorbing a sufficient amount of the fluid encountered in use of a diaper or other absorbent article. A polymer having a high gel strength generally possesses a low absorption capacity, and a polymer having a high absorption capacity typically possesses a low absorption rate because of gel blocking phenomenon or low gel swelling pressure.

Another characteristic that a superabsorbent polymer must possess is an acceptably low level of extractable, water soluble polymer remaining within the superabsorbent. The extractable polymer can leach out of a hydrogel when fluids contact the superabsorbent. So called extractable polymers contribute to a "wet feel" of the article, and slow fluid transport in the article resulting in leakage of fluid from the absorbent article.

Commercially available superabsorbents generally possess sufficient capacity, and absorption under pressure but do not have adequate gel strength, swell rate (i.e. absorption speed) and permeability under pressure for the absorbent articles of reduced size and thickness that are now being produced. As fluff fiber in absorbent products is replaced with greater amounts of superabsorbent polymer, the polymer has to perform the functions of the fluff fiber. The polymer must quickly absorb fluid and transport it throughout an absorbent article without releasing the stored fluid from the swelled hydrogel on exertion of pressure. Accordingly, the swollen gel particles cannot impede absorption of additional fluid by forming a barrier, but must maintain their liquid permeability.

In order to improve the absorption speed of superabsorbent polymers, blowing agents have been incorporated into superabsorbents as described in U.S. Pat. Nos. 5,118,719 and 5,145,713. As the blowing agent is dispersed throughout the monomer solution during polymerization, it releases carbon dioxide. The porosity of the resultant superabsorbent polymer provides more surface area within the polymer particles, increasing the rate at which fluid is absorbed by the polymer.

The absorption under pressure of a superabsorbent has been improved by crosslinking the molecular chains at the surface of the polymer. Surface crosslinkage also improved the gel strength of the polymer and reduces the amount of extractables at the polymer surface. Although capacity is reduced at the polymer surface, the core of the polymer, which has lower crosslink density, retains its absorbance capacity. Normally, surface crosslinking creates a random, fairly uniform shell of higher cross-link density. Surface crosslinkage, however, frequently reduces the absorption speed of the polymer. While these materials possess adequate absorption under pressure, they absorb significantly slower than the fluff fiber they are replacing in thinner personal care articles.

The polymers which have been crosslinked at their surface (herein referred to as core polymers) are not porous materials like those disclosed in U.S. Pat. Nos. 5,118,719 and 5,145,713. Accordingly, these superabsorbents generally exhibit slow rates of absorption. U.S. Pat. Nos. 4,666,983 and 5,140,076 disclose absorbent polymers formed from reacting an absorbent resin powder having a carboxyl group with a crosslinking agent having at least two functional groups per molecule to crosslink the surface of the polymer. German Patent No. 4,020,780 describes surface crosslinked superabsorbent particles formed by coating monomers having acid groups with an alkylene carbonate. U.S. Pat. No. 5,229,466 discloses surface crosslinking by treating a water swellable carboxyl group containing polymer with a solution of an N-(hydroxyalkyl)-beta-(meth)-alanine ester or a polycondensation product thereof. A superabsorbent polymer made from acrylic acid, a water soluble polysaccharide and a crosslinking monomer having at least two polymerizable ethylenically unsaturated double bonds per molecule is described in U.S. Pat. No. 5,145,906. Water absorbent resins surface treated with a polyquatemary amine are disclosed in U.S. Pat. No. 4,824,901.

Swollen gel permeabilities of commercial superabsorbent materials as measured by the test described herein (at 60 minutes) are often much less than 5 g/g, or less even for so called advanced materials. There is a need for superabsorbent materials having higher swollen gel permeability characteristics. Materials exhibiting higher gel permeability characteristics should and do exhibit properties allowing more efficient use of superabsorbent in articles by making use of a greater portion of the superabsorbent in the superabsorbent containing personal hygiene article. As an example, bodily fluids, such as urine in a baby diaper tend to be deposited in the crotch area of the diaper. One of the most difficult and limiting factors of diaper design is to have the diaper transport the urine away from the crotch, against the force of gravity, into the unused front and rear portions of the diaper. The driving force comes from the wicking and suction of other portions of the diaper. Most tests described in the literature measure swollen hydrogel permeability by passing an aqueous fluid through a confined, swollen hydrogel with gravity or a hydrostatic head as the driving force, for instance in U.S. Pat. No. 5,147,343. The test described herein more accurately requires the fluid to move against gravity through a compressed swollen matrix, with the driving force being the wicking ability and suction power of the hydrogel itself. The superabsorbent polymers described and claimed herein exhibit improved permeability, resulting in less leakage from personal care articles made therefrom, and greater use of the total of the superabsorbent in the article. There is accordingly a need for a method of producing a water absorbent resin which exhibits high absorbency under pressure, high absorption speed, high permeability under pressure, and high gel strength.

SUMMARY OF THE INVENTION

In order to satisfy the need for improved superabsorbents having greater absorption under pressure, high permeability under pressure, and fast absorption rate, one aspect of the present invention provides a superabsorbent polymer preparable by the process of first providing a solution containing carboxylic acid monomers or water soluble salts thereof, and a crosslinking agent, herein referred to as the monomer solution. A carbonate blowing agent and a polymerization initiator are added. individually or in combination, to the monomer solution to form a carbonated monomer solution. The carbonated monomer solution is then polymerized at temperatures ranging from about 0° C. to about 130° C., forming a microcellular hydrogel. The microcellular hydrogel is chopped or ground into gel pieces having a particle diameter ranging from about 0.1 mm to about 5.0 cm. The gel pieces are dried at temperatures ranging from about 85° C. to about 210° C., and are then ground to form a polymer having a particle size of from about 0.05 mm to about 5.0 mm. A mixture is formed from 100 parts by weight of the polymer and about 0.001 to about 30 parts by weight of a surface crosslinking agent. The polymer is reacted with the surface crosslinking agent to crosslink molecular chains existing on a surface of the polymer, forming the superabsorbent polymer.

Another embodiment of the present invention is a method of making a superabsorbent polymer having improved absorption under pressure, improved permeability under pressure and improved absorption rate when absorbing aqueous body fluids by the above identified process.

A third embodiment of the invention is a method of improving the absorption under pressure, permeability under pressure and absorption rate of a superabsorbent polymer. The superabsorbent polymer is made by the method as described above, and is then exposed to aqueous body fluids, when the superabsorbent polymer is under the exertion of pressure. The superabsorbent polymer can be contained within a diaper, an incontinence pad, a sanitary napkin or a bandage.

It is an object of this invention to provide a surface crosslinked superabsorbent polymer which exhibits improved absorption under pressure, and improved permeability under pressure while increasing the absorption rate of the polymer with or without an applied pressure.

An associated object of the invention is to provide a superabsorbent polymer having a core with a lower crosslink density as compared to the surface of the polymer such that the core retains its absorbent capacity.

Another object of the invention is to provide a superabsorbent polymer in which spacings exist between the polymer particles when swelled, allowing fluid to pass the swelled particles and travel throughout the absorbent article.

Yet another object of the invention is to provide superabsorbent polymer particles with better bulk, inter- and intra-particle permeability.

It is yet still another object of this invention to provide to the art a superabsorbent polymer having chemically stiffened pores which has high permeability under pressure.

Other objects will be apparent to those skilled in the art from the disclosure herein.

DETAILED DESCRIPTION OF THE INVENTION

The carboxylic containing superabsorbent polymers of this invention have a swell rate of at least 0.3 g./g.sec., a gel strength of about 40,000 to about 150,000 dynes/cm², a centrifuge capacity at 30 minutes of about 20 to about 50 g/g, an absorption permeability under pressure at 60 minutes of at least 5 g/g at wherein the ratio of the absorption permeability under pressure at 15 minutes is at least 25% of the absorption permeability under pressure at 60 minutes.

Preferably, the carboxylic containing superabsorbent polymers of this invention have a swell rate of from about 0.4 to about 1.5 g./g.sec., a gel strength of from about 50,000 to about 124,000 dynes/cm², a centrifuge capacity of about 25 to about 45 g/g, an absorption permeability under pressure at 60 minutes of at least 15 g/g wherein the ratio of the absorption permeability under pressure at 15 minutes is at least 40% of the absorption permeability under pressure at 60 minutes.

Most preferably, the carboxylic containing superabsorbent polymers of this invention have a swell rate of from about 0.5 to about 1.0 g./g.sec., a gel strength of from about 60,000 to about 100,000 dynes/cm², a 30 minute centrifuge capacity of from about 30 to about 40 g/g, an absorption permeability under pressure at 60 minutes of at least 15 g/g and wherein the ratio of the absorption permeability under pressure at 15 minutes is at least 50% of the absorption permeability under pressure at 60 minutes.

The present invention provides a hydrogel-forming superabsorbent polymer which can be incorporated in absorbent articles such as diapers, adult incontinence pads, sanitary napkins, and bandages. The polymer can be used to effectively replace fluff fiber within these products because the polymer quickly absorbs fluid and transports it throughout the product without releasing the stored fluid from the swelled hydrogel on exertion of pressure. The swollen gel particles do not impede absorption of additional fluid by forming a barrier, but maintain theft liquid permeability.

The superabsorbent polymer of the present invention may be prepared by first forming a monomer solution containing carboxylic acid monomers or water soluble salts thereof, and an effective water insolubilizing amount of a crossing agent. A carbonate blowing agent and a polymerization initiator are added, individually or in combination, to the monomer solution to form a carbonated monomer solution. The carbonated monomer solution is then polymerized to form a microcellular hydrogel. The microcellular hydrogel is chopped or ground into gel pieces which are then dried and ground to form a core polymer. High permeability of a superabsorbent polymer is believed related to the stiffness of pores in the core polymer. In order to obtain increased permeability, core polymer stiffness should be maximized to the extent that capacity is not inversely affected.

After the core polymer is made, it is surface crosslinked to provide superabsorbent particles having a low crosslink density within the particle core and chemically stiffened pores opening to the surface of the particle. A mixture is formed from 100 parts by weight of the core polymer and about 0.001 to about 30 parts by weight of a surface crosslinking agent. The core polymer is reacted with the surface crosslinking agent which is preferentially drawn into the pores creating the highest crosslinking density within the pores. Crosslinking of the molecular chains existing on a surface of the core polymer also occurs at this step, forming the superabsorbent polymer. It is through the surface crosslinking process that the chemically stiffened pores of this invention are obtained.

More specifically, the core polymer is formed in solution, or in a water-in-oil emulsion containing carboxylic acid containing monomers and a crosslinking agent. An effective microcellular forming amount of the carbonate blowing agent is added to the monomer solution to form the carbonated monomer solution.

A polymerization initiator is added to the monomer solution or the carbonated monomer solution for the purpose of initiating the reaction between the monomers and the crosslinking agent. The initiator is either added to the monomer solution immediately before or simultaneously with addition of the blowing agent, or is added to the carbonated monomer solution immediately after the blowing agent has been added to the monomer solution. The initiator is added within no more than five minutes before, or fifteen minutes after the addition of the carbonate blowing agent to the monomer solution. Simultaneous addition of both initiator and blowing agent, or addition of initiator after the addition of blowing agent is preferred.

The core polymer is preferably formed from a thin layer of the carbonated monomer solution, which has been deaerated (purged of oxygen). The thin layer solution is preferably deaerated and protected from air before polymerization, and after initiating polymerization by the addition of free radical catalysts or by ionizing radical forming radiation. The polymerization forms an aqueous hydrogel of the crosslinked, water insoluble polymer. The polymerization is exothermic, causing the gel temperature to increase from the initiator temperature of the carbonated monomer solution of about 0° C. to 20° C. to temperatures of about 80° C. to 130° C. The aqueous gel, in the presence of the carbonate blowing agent, develops a microcellular hydrogel as polymerization occurs because decomposition of the carbonate blowing agent upon heating and or reaction with carboxylic groups disperses carbon dioxide throughout the hydrogel.

The microcellular structure of the core polymer may appear cloudy (demonstrating relatively small dispersed gas bubbles), opaque (normally representing somewhat larger gas bubbles or higher quantities of carbon dioxide), or foamy. The microcellular gel volume increases range from about 1.01 to at least 10.0 times the volume of the carbonated monomer solution, primarily depending upon the concentration of the carbonate blowing agent contained in the carbonated monomer solution.

The microcellular gel is then masticated by chopping, grinding, or otherwise forming gel pieces have particle diameter sizes ranging from about 0.1 millimeter to about 5.0 centimeters, preferably about 10 millimeters to about 2.0 centimeters. These masticated gel pieces are then dried at temperatures ranging from about 85° C. to about 210° C. to form a dry superabsorbent core polymer. The core polymer is then ground to a particle size having a diameter of from about 0.05 millimeter to about 5.0 millimeters. The resultant core polymer as described in U.S. Pat. Nos. 5,154,713 and 5,118,719, which are incorporated herein by reference, exhibits an improved rate of absorption of aqueous fluids while essentially retaining the gel strength and capacity of conventional superabsorbents made without carbonate blowing agents.

After the core polymer is formed, the surface region of the core polymer is crosslinked using a surface crosslinking agent to obtain the superabsorbent polymer having chemically stiffened pores of the present invention. Surface crosslinking of the core polymer improves the absorption under pressure, permeability under pressure, absorption rate, and gel strength after absorption while maintaining an acceptable absorption capacity. The surface crosslinking agents for use in the present invention include organic carbonates, polyquatemary mines, multivalent cations and compounds possessing in the molecular unit thereof at least two functional groups capable of reacting with the carboxyl group of the core polymer. 100 parts by weight of the core polymer formed as described above are mixed with about 0.01 to about 30 parts by weight of a surface crosslinking agent, depending upon the selected core polymer, and the surface region of the core polymer is reacted with the surface crosslinking agent. The reaction can be carded out during and/or after mixing using a conventional mixer.

The reaction between the core polymer and the surface crosslinking agent may occur at room temperature as when an aziridine compound is selected as the surface crosslinker. Heat is preferably applied to promote the reaction although it is not required to effect the reaction in many instances. When heat must be applied for the reaction to occur as when a polyhydric alcohol, a polyglycidyl compound, a polyamine compound, or a polyoxazoline compound is used as the surface crosslinking agent have been mixed. The temperature of the heat treatment is generally in the range of 40° C. to 250° C., preferably in the range of 90° C. to 250° C. At temperatures exceeding 250° C. the core polymer could be subject to thermal deterioration. The mixture can be heated using conventional dryers or heating ovens.

The materials required to produce the superabsorbent polymers of the invention are specified below. The core polymer is formed using monomers in an aqueous solution, or monomers dissolved in water and then dispersed in a water-in-oil emulsion. The hydrogel-forming core polymer is normally synthesized from aqueous solutions containing acrylic acid, methacrylic acid, their water soluble salts, and mixtures thereof. The monomers are preferably dissolved in an aqueous solution containing the crosslinking agent. The monomer solution contains at least 20 percent by weight total monomer content, preferably about 25 to about 75 percent by weight total monomer content, and most preferably from about 30 to about 60 percent by weight total monomer content.

An olefinically unsaturated carboxylic acid and carboxylic acid anhydride monomers can be used to form the core polymer of the invention. Suitable monomers include acrylic acids and their anhydrides such as acrylic acid, methacrylic acid, ethacrylic acid, alpha-chloracrylic acid, alphacyanoacrylic acid, and beta-methyl acrylic acid. For purposes of the present invention, the term (meth)acrylic acid represents the presence of acrylic acid alone, methacrylic acid alone, any admixture of these acids, and any water soluble salt of these acids, either alone or in admixture. The unsaturated carboxylic acid monomers can also include itaconic acid, citraconic acid, maleic acid, fumaric acid, and maleic anhydride. These monomers can be chosen from but are not limited to, vinyl sulfonic acids, allyl sulfonic acids, allyl sulfonic acids, styrene esters including sulfoacrylic and methacrylic acid esters such as sulfoethylacrylate, sulfoethylmethacrylate, sulfopropylacrylate, and sulfopropylmethacrylate, and sulfo(meth)acrylamide materials such as acrylamido N-methylene sulfonic acid, acrylamido-N-ethylene sulfonic acid, and 2-acrylamide and methacrylamide are useful in forming copolymers which can be crosslinked to form a core polymer.

The monomers are preferably selected from the group consisting of acrylic acid, the water soluble salts of acrylic acid, methacrylic acid, the water soluble salts of methacrylic acid, and mixtures thereof. A preferred monomer mixture consists essentially of from 20 weight percent to 40 weight percent (meth)acrylic acid and from 60 weight percent to 80 weight percent sodium (meth)acrylate.

The core polymer is made from free acid, partially neutralized monomers, or is partially or completely neutralized either before or after polymerization by addition of appropriate base materials, such as sodium hydroxide, ammonia, and the like. Any suitable basic salt forming cation including the alkaline metals, ammonia, ammonium salts, and amines may be used for the purpose of neutralization.

It is preferred to have a degree of neutralization of the carboxylic acid monomers of at least 50 mole percent and up to about 60 to 80 mole percent. When appropriate, the degree of neutralization can be partially accomplished by the addition of the carbonate blowing agents.

Preferably, the carboxyl group is present in the core polymer in an amount of not less than 0.01 equivalent, based on 100 g of the core polymer. In the case of a partially neutralized polyacrylic acid, for example, the proportion of the unneutralized polyacrylic acid is preferably in the range of 1 to 50 mole percent.

The crosslinking agents that can be used to form the monomer solution include, but are not limited to, compounds having at least two polymerizable double bonds, compounds having at least one polymerizable double bond and at least one functional group reactive with the acid containing monomer material, and polyvalent metal compounds, which metallic cations can form ionic crosslinkages. Crosslinking agents containing at least two polymerizable double bonds include di, tri or polyvinyl compounds such as divinyl benzene and divinyl toluene, di, tri or polyesters of unsaturated mono or poly carboxylic acids with polyols including di or tri acrylic acid esters of polyols such as ethylene glycol, trimethylpropane, glycerine, and polyoxyethylene glycols. Other crosslinking agents can include alkylene bis-acrylamides such as N, N'-methylene-bis-acrylamide, carbamyl esters obtained by reacting polyisocyanates with hydroxyl group containing monomers, di, tri or poly allyl esters of polyols, di, tri or poly allyl esters of polycarboxylic acids such as diallyl phthalate and diallyl adipate, poly carboxylic acid polyols such as trimethylolpropane triacrylate, esters of unsaturated mono or poly-carboxylic acids with monoallyl esters of polyols such as the acrylic acid ester of polyethylene glycol monoallyl ether, and di or triallyl amine, and the alkylene glycol diglycidyl ethers.

The crosslinking agent is present in an amount ranging from about 0.005 weight percent of the monomer solution to about 2.0 weight percent of the monomer solution. As stated earlier, it is important to obtain increased permeability to chemically stiffen pores contained in the core polymer. In a preferred mode of practicing this invention at least 0.08% by weight (800 ppm) of cross linking agent is added to the monomer solution, and most preferably at least 0.13% by weight (1300 ppm) of cross linking agent is added based on the weight of the monomer solution. While there is no specific upper limit as to the amount of crosslinker that may be added, amounts greater than about 2-5% by weight of the monomer solution are undesirable because of the decrease in capacity that is caused by excessive crosslinking.

The most preferred crosslinking agents are bis-acrylamides such as N-N'-methylene bisacrylamide, the di, tri or polyesters of unsaturated mono or poly carboxylic acid polyols such as trimethylolpropane triacrylate, the di or tri glycidyl ethers of polyols such as ethylene glycol diglycidyl ether, the multi-substituted allyl amines such as diallyl amine and triallyl amine, or mixtures thereof.

Carbonate blowing agents are added to the monomer solution to form the carbonated monomer solution. The blowing agent releases carbon dioxide when reacted with acid in the monomer solution. The blowing agent can be any carbonate or bicarbonate containing salt or mixed salt, and may include carbon dioxide as a gas or a solid, sodium carbonate, potassium carbonate, ammonium carbonate, magnesium carbonate, or magnesium (hydroxic) carbonates, calcium carbonate, barium carbonate, sodium bicarbonate, potassium bicarbonate, ammonium bicarbonate, and their hydrates, or other cations, as well as naturally occurring carbonates, such as dolomite, and mixtures thereof. Preferred carbonate blowing agents are monovalent carbonate salts such as sodium and potassium carbonate. Sodium carbonate is an especially preferred blowing agent for use in this invention.

Other preferred blowing agents are carbonate salts of multivalent cations such as magnesium, calcium, and zinc. Although many of the multivalent transition metal cations can be used, some of them, such as ferric cation, can cause staining and may be subject to reduction-oxidation reactions or hydrolysis equilibria in water. This may lead to difficulties in quality control of the final polymeric product. Also, other multi-valent cations such as nickel, barium, cadmium, and mercury would be unacceptable because of potential toxic or skin sensitizing effects.

It is preferred to add from about 0.05 to about 2.5 weight percent blowing agent based on the weight of the monomer solution. It is most preferred to add from about 0.2 weight percent to about 2.5 weight percent blowing agent. The blowing agents must be added immediately before or immediately after polymerization is initiated. The blowing agents are not effective if added after the hydrogel is formed, nor is it effective when added after chopping or drying the gelled polymer.

The polymerization of the carbonated monomer solution is initiated with free radical catalysts which are well known in the art. These initiators may include, but are not limited to, peroxide or persulfate catalysts, azo catalysts, the so called redox catalysts, or any combination thereof. Preferred catalysts include hydrogen peroxide, sodium persulfate, organic peroxides, sodium bisulfite, peracetate catalysts, azo catalysts and mixtures thereof.

While it is preferred to treat the resultant core polymer materials of this invention with surface crosslinking agent, one of the important features of this invention is the formation of a core polymer, prior to surface crosslinking with increased absorption speed, gel strength and permeability. Thus, surface crosslinking is a preferred treatment, but, the invention yields a core polymer having improved properties as well.

The surface crosslinking agents for use in the present invention include organic carbonates, polyquatemary amines, polyvalent metal compounds and compounds possessing in the molecular unit thereof at least two functional groups capable of reacting with the carboxyl group of the core polymer. The surface crosslinking agents include polyhydric alcohols such as ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, polyethylene glycol, glycerin, polyglycerol, propylene glycol, diethanolamine, triethanolamine, polyoxypropylene, oxyethylene-oxypropylene oxypropylene block copolymer, sorbitan fatty acids esters, polyoxyethylene sorbitan fatty acid esters, trimethylolpropane, pentaerythritol, polyvinyl alcohol and sorbitol, polyglycidyl ether compounds such as ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, glycerin diglycidyl ether, glycerol polyglycidyl ether, pentaerythritol polyglycidyl ether, propylene glycol diglycidyl ether, and polypropylene glycol diglycidyl ether, polyaziridine compounds such as 2,2-bishydroxymethylbutanol-tris[3-(1-aziridinyl)propionate], 1,6-hexamethylene diethylene urea, and diphenylmethane-bis-4,4'-N,N'-diethylene urea, haloepoxy compounds such as ethylene diamine, diethylene triamine, triethylene tetramine, tetraethylene pentamine, pentaethylene hexamine, and polyethylene imine, polyisocyanate compounds such as 2,4-tolylene diisocyanate and hexamethylene diisocyanate, hydroxides of zinc, calcium, magnesium, aluminum, iron, titanium and zirconium, halogenides, alkylene carbonates such as 1,3-dioxolan-2-one and 4-methyl-1,3-dioxolan-2-one, polyvalent metal compounds such as salts, (represented by sulfates), for example, and polyquatemary amines such as condensation products of dimethylamine and epichlorohydrin, homo and copolymers of diallyldimethyl ammonium chloride, and homo and copolymers of dimethylaminoethyl(meth)acrylate methyl chloride quaternary ammonium salts. One crosslinking agent or two or more mutually unreactive crosslinking agents selected from the group mentioned above are used.

Preferably, the surface crosslinking agent includes at least one compound selected from the group consisting of diethylene glycol, triethylene glycol, polyethylene glycol, glycerin, polyglycerin, propylene glycol, diethanolamine, triethanolamine, polyoxypropylene, oxyethylene-oxypropylene block copolymer, sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, trimethylol propane, pentaerythritol, polyvinyl alcohol, sorbitol, ethylene carbonate, and ethylene glycol diglycidyl ether. The crosslinking agent is used in an amount ranging from about 0.01 to about 30 parts by weight, preferably about 0.1 to about 10 parts by weight, based upon 100 parts by weight of the core polymer.

Organic solvents or water can be added as the core polymer and the surface crosslinking agent are mixed to promote uniform dispersion. The amount of water to be used is in the range of 0 to about 50 parts by weight, preferably up to about 40 parts by weight, more preferably up to about 20 parts by weight, based upon 100 parts by weight of the core polymer. Even less water than 20 parts by weight per 100 parts of polymer can be used. In the practice of this invention, as little as 0.25-5 parts of water per 100 parts of polymer can be used. If the amount of water exceeds 50 parts by weight, drying time is increased and the surface crosslinking agent permeates to the center of the core polymer particles, reducing the absorption capacity.

Organic solvents can be added to the mixture in an amount of 0 to about 60 parts by weight, preferably up to about 10 parts by weight, based upon 100 parts by weight of the core polymer. Amounts of solvent in excess of 60 parts by weight increase the required drying time of the superabsorbent. The organic solvents include lower alcohols such as methanol, ethanol, n-propanol, isopropanol, n-butanol, isobutanol, secbutanol, and t-butanol, ketones such as acetone, methylethyl ketone and methylisobutyl ketone, ethers such as dioxane, tetrahydrofuran and diethyl ether, amides such as N,N-dimethyl formamide and N,N-diethyl formamide, and sulfoxides such as dimethyl sulfoxide.

Absorbent articles such as diapers, adult incontinence pads, sanitary napkins and bandages may have a core entirely composed of the superabsorbent polymer of the present invention, or can include polymer layers comprised of up to 100% of the superabsorbent polymer within the core material.

The following examples are presented to describe preferred embodiments and utilities of the present invention are not meant to limit the present invention unless otherwise stated in the claims appended hereto.

EXAMPLE 1

The following test methods were performed to determine the characteristics of the tested polymers:

A. Gel Strength

Gel Strength was determined by placing 3.00 g. of superabsorbent polymer in an excess of GS synthetic urine (7.50 parts 1% aqueous solution of Triton®X-100, 30.00 parts NaCl, 0.68parts anhydrous CaCl₂, 1.80 parts MgCl₂ 6H₂ O and 3000 parts deionized water) for 10 minutes while stirring. The excess fluid is then removed from the swollen gel by blotting for one minute with paper toweling. The now blotted gel is placed between the parallel plates in the test cylinder of a Rank Pulse Shearometer, distributed by PenKem, Inc., Bedford Hills, N.Y.). The time required for a high frequency torsional shear wave to pass through the gel is measured at plate gaps of 12-14mm in 1 mm increments. The gel strength or shear modulus (G') is calculated from the velocity of the shear wave by standard techniques.

B. Centrifuge Capacity

Centrifuge capacity is calculated by placing 0.2000±0.005 grams of polymer in a 2 inch×2 inch tea bag and sealing the bag. An empty bag is also sealed and used as a blank. The bags are then placed in a crystallizing dish containing 300 milliliters of SynUrine test solution, (650 ppm Na⁺, 70 ppm Ca²⁺, 60 ppm Mg²⁺, 1150 ppm K⁺, 260 ppm phosphorus, 475 ppm sulfur, 1200 ppm chloride and 1350 ppm sulfate in aqueous solution) and allowed to absorb fluid for 30 minutes. The tea bags are then removed from the crystallizing dish, centrifuged at 1500 rpm for 3 minutes and weighed. Centrifuge capacity is calculated as follows:

    Centrifuge Capacity(g/g) =A-B-C

Where A=mass of swollen gel and tea bag after centrifugation

B=mass of blank (empty tea bag) after centrifugation

C=mass of dry superabsorbent polymer

C. Swell Rate

Swell rate is determined by screening 0.358±0.001 grams polymer to a -20/+50 mesh particle size, weighing the polymer and placing it in a 16 mm test tube. 10.0 grams of synthetic urine are added to the tube at time zero. The time required for the gel to swell to the bottom of the fluid meniscus is recorded. The swell rate is calculated by dividing the mass of fluid absorbed by the mass of the polymer used and the time required to absorb the fluid.

D. Absorption Under Pressure

Absorption Under Pressure (AUP) is determined by placing a 120 mm diameter flitted disk (Schott-Ceramic Filter Duran; diameter=120mm; porosity=0) in a crystallizing dish having a diameter of 200 mm and a height of 75 mm. Synthetic urine of the type used to determine Centrifuge Capacity above is added to the dish to cover the disk, and the disk is allowed to equilibrate for several minutes. Synthetic urine is then removed so that that the top surface of the disk is even with the liquid meniscus. A piece of round filter paper, Whatman #1; diameter 125 mm is then placed on the fritted disk, and the filter paper is allowed to become saturated with the synthetic urine. 0.9000 grams of superabsorbent polymer to be evaluated is then sprinkled uniformly on a 400 mesh screen filter cloth at the bottom of a plexiglass cylinder having an inner diameter of 61 mm, and a height of 50 mm. A plastic piston/cup having a diameter of 60 mm which fits inside the cylinder is then placed in the cylinder. Weight placed on the cup is varied depending on the pressure at which permeability under pressure is to be measured. Conducting the test at 0.7 psi is preferred. A weight of 596 g (cup+weight) is used for 0.3 psi, a weight of 1390 g (cup+weight) is used for 0.7 psi. The weight of the completed cylinder group, including the polymer is recorded as "A". The cylinder group is then placed upon the wet filter paper, allowing the apparatus to absorb for 1 hour. The cylinder group is then removed from the crystallizing dish and reweighed CB). The absorption under pressure is then calculated: ##EQU1## where A=dry weight of the cylinder group including dry superabsorbent polymer;

B=weight of the cylinder group after 60 minute absorption; and.

X=dry weight of superabsorbent polymer sample.

E. Absorption Permeability Under Pressure (APUP)

Continuing the process for Absorption Under Pressure (AUP) above, After weighing the cylinder group and obtaining "B", the weight and piston are removed from the cylinder and 0.9000 grams of dry superabsorbent polymer are carefully and uniformly sprinkled onto the first layer of now swollen superabsorbent polymer. The piston and weight are now replaced and the complete cylinder group is placed back on the filter paper in contact with the synthetic urine in the crystallizing dish. The weight of the cylinder group ("C") is recorded periodically for 60 minutes, often at 10 minute intervals. Additional synthetic urine is added to the bath as needed to maintain a level equal to the top of the fritted disk.. The APUP (g/g) is calculated in a similar manner as the AUP in accordance with the following equation: ##EQU2## where:

B is the weight of the cylinder group after 1 st 60 minute AUP absorption;

C_(n) is the weight of the cylinder group after additional permeability absorption (at time interval "n", several time intervals up to 60 minutes may be evaluated); and,

Y is the weight of the second dry polymer sample added.

The final APUP value for permeability is generally taken after 60 minutes.

Aqueous monomer solutions containing about 30 to 40 weight percent of a combination of acrylic acid and sodium acrylate in a ratio of about 30:70 and triallyl amine crosslinking agent in the amounts specified in Table 1 were formed. The samples were polymerized without incorporation of a blowing agent. The resultant gel was ground and dried, and the characteristics of the nonporous core polymer were measured using the tests described above for determining gel strength, capacity and swell rate. These results are reported as samples 1 and 3 in Table 1. The nonporous core polymers of samples 1 and 3 were then surface crosslinked by reacting the polymers with from about 1 to about 3 weight percent ethylene carbonate to form the superabsorbent polymers of samples 2 and 4, respectively. The gel strength, capacity and swell rate for the samples are listed as follows:

                                      TABLE 1                                      __________________________________________________________________________                                AUP   AUP                                                    Swell Rate                                                                           Gel Strength                                                                          Capacity                                                                            @ 5 min.                                                                             @ 60 min.                                     Sample   (g./g.sec.)                                                                          (dynes/cm.sup.2)                                                                      (g/g)                                                                               (g/g) (g/g)                                         __________________________________________________________________________     1: 900 ppm                                                                              0.21  33,535 47.9  4.3 (.3 psi)                                                                         8.4 (.3 psi)                                 crosslinker, no             4.1 (.7 psi)                                                                         7.7 (.7 psi)                                 blowing agent                                                                  2: surface                                                                              0.17  55,400 39.7 26.1 (.3 psi)                                                                        33.1 (.3 psi)                                 crosslinked                17.0 (.7 psi)                                                                        20.4 (.7 psi)                                 Sample 1                                                                       3: 2500 ppm                                                                             0.28  77,310 35.6  6.5 (.3 psi)                                                                        22.4 (.3 psi)                                 crosslinker, no             4.4 (.7 psi)                                                                         9.0 (.7 psi)                                 blowing agent                                                                  4: surface                                                                              0.23  99,100 30.0 29.6 (.3 psi)                                                                        34.9 (.3 psi)                                 crosslinked                24.7 (.7 psi)                                                                        28.9 (.7 psi)                                 Sample 3                                                                       __________________________________________________________________________

After the surfaces of the nonporous core polymers were crosslinked, the swell rate and capacity, were reduced while the gel strength and absorption under pressure substantially improved.

EXAMPLE 2

Aqueous monomer solutions containing about 30 to 40 weight percent of a combination of acrylic acid and sodium acrylate in a ratio of about 30:70 and triallyl amine crosslinking agent in the amounts specified in Table 2 were formed. The samples were polymerized without incorporation of a blowing agent. The resultant gel was ground and dried, and the characteristics of the nonporous core polymer were measured using the tests described above for determining gel strength, capacity and swell rate. These results are reported as samples 1,3 and 5 in Table 2. The nonporous core polymers of samples 1.3 and 5 were then surface crosslinked by reacting the polymers with from about 3 weight percent glycerol to form the superabsorbent polymers of samples 2, 4 and 6, respectively. The gel strength and swell rate for the samples are listed below:

                  TABLE 2                                                          ______________________________________                                                             Swell Rate                                                                               Gel Strength                                     Sample              (g./g.sec.)                                                                              (dynes/cm.sup.2)                                 ______________________________________                                         1: 900 ppm crosslinker, no blowing                                                                 0.20      60,360                                           agent                                                                          2: Surface crosslinked Sample 1                                                                    0.27      58,815                                           3: 1500 ppm crosslinker, no blowing                                                                0.21      62,910                                           agent                                                                          4: Surface crosslinked Sample 3                                                                    0.33      66,785                                           5: 1500 ppm crosslinker, no blowing                                                                0.27      67,230                                           agent                                                                          6: Surface crosslinked Sample 5                                                                    0.39      69,015                                           ______________________________________                                    

After the surfaces of the nonporous core polymers were crosslinked, the swell rate unexpectedly improved, and the gel strength improved.

EXAMPLE 3

Aqueous monomer solutions containing about 30 to 40 weight percent of a combination of acrylic acid and sodium acrylate in a ratio of about 30:70 and triallyl amine crosslinking agent in the amount specified in Table 3 were formed. 0.4 weight percent Na₂ CO₃ blowing agent was added to the monomer solution, forming a carbonated monomer solution. The samples were polymerized and the resultant micorcellular gel was ground and dried. The characteristics of the porous core polymer were measured using the tests described above for determining gel strength, capacity and swell rate. These results are reported as samples 1, 3 and 5 in Table 3. The porous core polymers of samples 1, 3 and 5 were then surface crosslinked by reacting the polymers with from about 1 to about 3 weight percent glycerol to form the superabsorbent polymers of samples 2, 4 and 6, respectively. The gel strength, capacity and swell rate for the samples are listed below:

                                      TABLE 3                                      __________________________________________________________________________                                           APUP  APUP                                       Swell             AUP   AUP   @ 15 min.                                                                            @ 60 min.                                  Rate  Gel Strength                                                                          Capacity                                                                            @ 5 min.                                                                             @ 60 min.                                                                            (g/g) (g/g)                              Sample  (g./g.sec.)                                                                          (dynes/cm.sup.2)                                                                      (g/g)                                                                               (g/g) (g/g) (0.7 psi)                                                                            (0.7 psi)                          __________________________________________________________________________     1: 1,400 ppm                                                                           0.49  48,845 42.5  4.8 (.3 psi)                                                                        10.2 (.3 psi)                                  crosslinker,               4.0 (.7 psi)                                                                         8.0 (.7 psi)                                  blowing agent                                                                  2: surface                                                                             0.57  69,760 35.5 30.6 (.3 psi)                                                                        37.5 (.3 psi)                                                                        2.4   6.1                                crosslinked               11.4 (.7 psi)                                                                        20.4 (.7 psi)                                  Sample 1                                                                       3: 2000 ppm                                                                            0.47  67,470 39.1  5.1 (.3 psi)                                                                        12.9 (.3 psi)                                  crosslinker,               4.1 (.7 psi)                                                                         8.2 (.7 psi)                                  blowing agent                                                                  4: surface                                                                             0.58  79,245 33.1 33.8 (.3 psi)                                                                        36.7 (.3 psi)                                                                        5.3   16.4                               crosslinked               21.0 (.7 psi)                                                                        29.4 (.7 psi)                                  Sample 3                                                                       5: 2,500 ppm                                                                           0.51  76,785 35.9  6.4 (.3 psi)                                                                        18.1 (.3 psi)                                  crosslinker,               4.1 (.7 psi)                                                                         8.4 (.7 psi)                                  blowing agent                                                                  6: Surface                                                                             0.67  95,755 30.1 33.4 (.3 psi)                                                                        34.9 (.3 psi)                                                                        12.4  27.6                               crosslinked               23.3 (.7 psi)                                                                        28.7 (.7 psi)                                  Sample 5                                                                       __________________________________________________________________________

After the surfaced of the porous core polymers were crosslinked, the swell rate, gel strength and absorption under pressure substantially improved. Although the capacity was reduced, it remained within an acceptable range. When the characteristics of the superabsorbents derived from the porous core polymers are compared to those derived from the nonporous core polymers of Example 1, it is evident that incorporation of a blowing agent in the core polymer improved the swell rate of the polymer even though the swell rate, in most instances, would have declined after surface crosslinking. When compared to the nonporous core polymers of Example 2, the swell rates of the superabsorbents derived from porous core polymers were two to three times greater than those of Example 2.

While the invention is susceptible to various modifications and alternative forms, specific embodiments thereof have been shown by way of example and were herein described in detail. It should be understood, however, that it is not intended to limit the invention to the particular forms disclosed, but on the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the invention as defined by the appended claims.

EXAMPLE 4

Additional experiments were run similar to Example 3. These experiments were performed at a slightly later time than the experiments set forth in Example 3 but followed the same general synthetic routes. Results are shown on Table 4.

                                      TABLE 4                                      __________________________________________________________________________                               AUP   AUP   APUP  APUP                                       Swell             @ 5 min.                                                                             @ 60 min.                                                                            @ 15 min.                                                                            @ 60 min.                                  Rate  Gel Strength                                                                          Capacity                                                                            (g/g) (g/g) (g/g) (g/g)                              Sample  (g./g.sec.)                                                                          (dynes/cm.sup.2)                                                                      (g/g)                                                                               (0.7 psi)                                                                            (0.7 psi)                                                                            (0.7 psi)                                                                            (0.7 psi)                          __________________________________________________________________________     1: 1,300 ppm                                                                           0.56  --     34   25.7  29.9  13.1  21.9                               crosslinker,                                                                   blowing agent                                                                  and surface                                                                    crosslinker                                                                    2: 2,500 ppm                                                                           0.73  --     30   30.0  31.6  17.5  26.8                               crosslinker,                                                                   blowing                                                                        agent, and                                                                     surface                                                                        crosslinker                                                                    __________________________________________________________________________

Results again indicate that the process of the subject invention, including the use of blowing agent, and surface cross linking agent provides a material having a superior APUP. 

We claim:
 1. A carboxylic containing superabsorbent polymer having a swell rate of at least 0.3 g./g.sec., a gel strength of about 40,000 to about 150,000 dynes/cm², a centrifuge capacity at 30 minutes of about 20 to about 50 g/g, an absorption permeability under pressure at 60 minutes of at least 5 g/g at wherein the ratio of the absorption permeability under pressure at 15 minutes is at least 25% of the absorption permeability under pressure at 60 minutes.
 2. The carboxylic containing superabsorbent polymer of claim 1 having a gel strength of about 50,000 to about 124,000 dynes/cm².
 3. The carboxylic containing superabsorbent polymer of claim 1 having a swell rate of from about 0.4 to 1.5 g./g.sec.
 4. The carboxylic containing superabsorbent polymer of claim 1 having a centrifuge capacity at 30 minutes of from about 25 to about 45 g/g.
 5. The carboxylic containing superabsorbent polymer of claim 1 having an absorption permeability under pressure at 60 minutes of at least 15 g/g.
 6. The carboxylic containing superabsorbent polymer of claim 1 having a ratio of the absorption permeability tinder pressure at 15 minutes of at least 40%.
 7. The carboxylic containing superabsorbent polymer having a swell rate of from about 0.4 to about 1.5 g/g.sec., a gel strength of about 50,000 to about 124,000 dynes/cm², a centrifuge capacity at 30 minutes of about 25 to about 45 g/g, an absorption permeability under pressure at 60 minutes of at least 15 g/g wherein the ratio of the absorption permeability under pressure at 15 minutes is at least 40% of the absorption permeability under pressure at 60 minutes.
 8. The carboxylic containing superabsorbent polymer of claim 7 having a gel strength of about 60,000 to about 100,000 dynes/cm².
 9. The carboxylic containing superabsorbent polymer of claim 7 having a swell rate of from about 0.5 to 1.0 g./g.sec.
 10. The carboxylic containing superabsorbent polymer of claim 7 having a centrifuge capacity at 30 minutes of from about 30 to about 40 g/g.
 11. The carboxylic containing superabsorbent polymer of claim 7 having a ratio of the absorption permeability under pressure at 15 minutes of at least 50%.
 12. A carboxylic containing superabsorbent polymer having a swell rate of from about 0.5 to about 1.0 g/g.sec., a gel strength of about 60,000 to about 100,000 dynes/cm², a centrifuge capacity at 30 minutes of about 30 to about 40 g/g, an absorption permeability under pressure at 60 minutes of at least 15 g/g wherein the ratio of the absorption permeability under pressure at 15 minutes is at least 50% of the absorption permeability under pressure at 60 minutes. 